TDS-Araldite 2014-Epoxy

Flexural Modulus

631,475 psi (4355 MPa)

Tensile strength (ISO R527) at 73 o F (23 ° C)

3,773 psi (26 Mpa)

Elongation at break

0.7%

Lap shear strength versus immersion in various media (typical average values) Unless otherwise stated, L.S.S. was determined after immersion for 90 days at 73 o F (23 ° C) Cure: 16 hour / 104 o F (40°C)

30 days

60 days

90 days

psi

As-made value

2764 2799 3191 3336 2321 2741 2357 2756 2450 2812 2094

IMS

222 560

513

Gasoline

1213 2611 1691 1971 2031 3336

Ethyl acetate

2321

Acetic acid, 10%

793

Xylene

1492 2176 2321

Lubricating oil

Paraffin

Water at 73°F Water at 140°F Water at 194°F

3549 1015

2889 2715

Lap shear strength versus tropical weathering (40/92, DIN 50015; typical average values) Cure: 16 hours / 104°F (40 ° C)

Test: at 73°F (23 ° C)

psi

As made value After 30 days After 60 days After 90 days

2708 3078 3191 2901

Lap shear strength versus heat aging Cure : 16 hours / 104°F (40 ° C)

psi

As-made value 30 days / 158°F 60 days / 158°F 90 days / 158°F

2712 2843 2654 3017

Araldite ® 2014

Oct 2014

4/5